Product name:Good Quality Perlite Fireproof Fire Door Core
1.Description
OCM Fire Door Core board with thickness from 3mm to 25mm,can be applied in every part of a fire door.
The Diversity, non-combustibility, insulation and timber-like properties make OCM Fire Door Core board ideal for fireproof or fire retardant door frames, door panels, door studs, substrates, decorative boards of fire doors.It does not warp, or distort while continuous exposure to open fire for testing , prior to physical disintegration.
2.Component
•Using Magnesium Sulfate (MgSO4) instead of magnesium chloride , which makes the board Anti halogenation and also solve the rust problem.
•Made of mineral magnesium oxide, magnesium sulfate,(Mgoso4) Fiber glass, Perlite etc.
3.Features
•Outstanding fire behavior meet 30mins to 270mins.
•Lightness
•Stiffness
•A1 Incombustible level
•Durability
4.Specification
MGO Board
Thickness(mm) |
3mm,6mm,9mm,12mm,18mm |
Standard size: |
1220*2440/2700mm,910*2100mm,900*2200mm |
Special sizes |
available by special order |
Color |
white, grey. green and red. |
Mgo Perlite Board
Thickness(mm) |
38mm,43mm,48mm,50mm |
Standard Size: |
1220*2440mm,900*2100/200mm, |
Special Size: |
Available by special order |
5.Technical datas
Heading |
Unit Used |
Inspection value |
Standard |
Density |
Kg/m³ . |
0.96-1.12g/cm³ |
GB/T7019-1997 |
Fire ratings |
Grade |
A1 |
GB 8624 |
Thermal Resistance |
M² K/W |
1.14m² K/w |
GB/T13475-92 |
Bending Resistance (Dry) |
≤ Mpa |
18Mpa |
GB/T7019-1997 |
Bending Resistance (Fully Absorbed in Water) |
≤ Mpa |
22Mpa |
GB/T7019-1997 |
Sound Insulation |
DB |
≥ 44dB |
GBJ121-88 |
Absorption Moisture |
≤ % |
≤ 15% |
GB/T7019-1997 |
Tensile Strength |
≤ Mpa |
8-13Mpa |
GB/T7019-1997 |
Impact Resistance |
Kj/m² |
Between 2.0-2.5 are qualified,
For 4mm, our board could reach 4.5 kj/m2.
So our boards are good. |
CNS 13778 |
Mgo Perlite Board
Item |
Data |
Density |
300kg/m3,tolerance +-10kg/m3 or 500kg/m3 customized |
Folding strength |
≥ 8Mpa |
Compressive strength |
0.35-0.8(Mpa) |
Thermal conductivity |
≤ 0.035-0.076W(m.k) |
Moisture content |
≤ 10 |
Welling rate |
≤ 0.25 |
Fireproof limit |
0.6-4h |
Fireproof temperature |
1200c |
Sound-absorption coefficient |
0.03-0.8 |
6.Application
Mgo door core is ideal materials for fire door core and frame.